The manufacturer’s inadequate cleaning of the crucible before melting the nickel alloy used in casting the low pressure turbine stage 3 blades that resulted in a casting anomaly from where an intergranular crack occurred became the origin of a fatigue crack that led to the fracture of a low pressure turbine stage 3 blade.